| Raw material description section |
| Specification level |
Glass fiber reinforced grade |
Appearance color |
|
| Use of the material |
For mechanical parts, medium rigid cover, electrical insulation products |
| Remark |
Glass fiber reinforced type, easy to flow |
|
| |
| Performance item |
Test condition [state] |
Test method |
Test data |
Data unit |
| Mechanical properties |
Elongation at break |
Dry |
ISO527 |
5.8 |
% |
| Notched impact strength of cantilever beam |
Dry |
ISO180 |
9.5 |
KJ/m2 |
| Tensile strength |
Dry |
ISO527 |
139.3 |
MPa |
| Flexural modulus |
Dry |
ISO178 |
3.6 |
GPa |
| Tensile modulus |
Dry |
ISO527 |
4.6 |
GPa |
| Charpy impact strength |
Dry |
ISO179 |
55.8 |
KJ/m2 |
| Bending strength |
Dry |
ISO178 |
173.0 |
MPa |
| Charpy Notched Impact Strength |
Dry |
ISO180 |
13.6 |
KJ/m2 |
| Electrical properties |
Dielectric strength |
Dry |
IEC243 |
-- |
Kv/mm |
| Volume resistivity |
Dry / wet state |
IEC93 |
-- |
Ω.cm |
| Thermal property |
Linear expansion coefficient |
|
ISO11359 |
2.0-3 |
10-5K |
| Mfr |
Dry |
ISO1133 |
17.4 |
g/10min |
| Hot deformation temperature |
1.80MPa |
ISO75 |
247.1 |
℃ |
| Melting process |
Dry |
ISO3146 |
254-264 |
℃ |
| Other performance |
Plastic shrinkage |
Parallel |
- |
- |
0.05 |
% |
| vertical |
- |
- |
1.0 |
% |
| Water absorption rate |
23℃ Saturated |
ISO62 |
-- |
% |
| Density |
|
ISO1183 |
1.28 |
g/cm3 |
| Flame retardant |
|
UL94 |
HB |
|
|
|
|
|
|
|
|
|
|